Corrosion-resistant alloys:
Nickel-Base:
Alloy
|
Nia
|
Co
|
Fe
|
Cr
|
Mo
|
W
|
Mn
|
Si
|
Cb
|
V
|
Al
|
Ti
|
C
|
Cu
|
Others
|
B-2
|
69
|
1*
|
2*
|
1*
|
28
|
0.5*
|
1*
|
0.1*
|
-
|
-
|
-
|
-
|
0.01*
|
0.5*
|
-
|
B-3®
|
65b
|
3*
|
1.5
|
1.5
|
28.5
|
3*
|
3*
|
0.1*
|
0.2*
|
0.2*
|
0.5*
|
0.2*
|
0.01*
|
0.2*
|
Ta-0.2*, Zr-0.01*
|
C-4
|
65
|
2*
|
3*
|
16
|
16
|
-
|
1
|
0.08*
|
-
|
-
|
-
|
0.7*
|
0.01*
|
0.5*
|
-
|
C-22®
|
56
|
2.5*
|
3
|
22
|
13
|
3
|
0.5*
|
0.08*
|
-
|
0.35*
|
-
|
-
|
0.01*
|
0.5*
|
-
|
C-22HS® |
61 |
1* |
2* |
21 |
17 |
1* |
0.8* |
0.08* |
- |
- |
0.5* |
- |
0.01* |
0.5* |
- |
C-86
|
58
|
-
|
5*
|
21
|
16
|
4
|
1*
|
0.08*
|
-
|
-
|
0.5*
|
0.25*
|
0.01*
|
0.5*
|
-
|
C-276
|
57
|
2.5*
|
5
|
16
|
16
|
4
|
1*
|
0.08*
|
-
|
0.35*
|
-
|
-
|
0.01*
|
0.5*
|
-
|
C-2000®
|
59
|
2*
|
3*
|
23
|
16
|
-
|
0.5*
|
0.08*
|
-
|
-
|
0.5*
|
-
|
0.01*
|
1.6
|
-
|
G-30®
|
43
|
5*
|
15
|
30
|
5.5
|
2.5
|
1.5*
|
0.8*
|
0.8
|
-
|
-
|
-
|
0.03*
|
2
|
-
|
G-35®
|
58
|
1*
|
2*
|
33.2
|
8.1
|
0.6*
|
0.5*
|
0.6*
|
-
|
-
|
0.4*
|
-
|
0.05*
|
0.3*
|
-
|
G-50®
|
50b
|
2.5*
|
17
|
20
|
9
|
1*
|
1*
|
1*
|
0.5*
|
-
|
0.4*
|
-
|
0.02*
|
0.5*
|
-
|
HYBRID-BC1® |
62 |
1* |
2* |
15 |
22 |
- |
0.25 |
0.08* |
- |
- |
0.5* |
- |
0.01* |
- |
- |
N
|
71
|
0.2*
|
4*
|
7
|
16
|
0.5*
|
0.8*
|
1*
|
-
|
0.5*
|
-
|
-
|
0.06
|
0.35*
|
(Al+Ti)-0.5*
|
aAs balance bMinimum cCb+Ta *Maximum
Cobalt-Base:
Alloy
|
Coa
|
Ni
|
Fe
|
Cr
|
Mo
|
W
|
Mn
|
Si
|
N
|
C
|
ULTIMET®
|
54
|
9
|
3
|
26
|
5
|
2
|
0.8
|
0.3
|
0.08
|
0.06
|
aAs balance bMinimum cCb+Ta *Maximum
High-temperature Alloys:
Nickel-Base:
Alloy
|
Nia
|
Co
|
Fe
|
Cr
|
Mo
|
W
|
Mn
|
Si
|
Cb
|
Al
|
Ti
|
C
|
B
|
Zr
|
Cu
|
Others
|
75
|
76
|
-
|
5*
|
20
|
-
|
-
|
1*
|
1*
|
-
|
0.4*
|
0.4
|
0.11
|
-
|
-
|
0.5*
|
-
|
214®
|
75
|
2*
|
3
|
16
|
0.5*
|
0.5*
|
0.5*
|
0.2*
|
0.15*
|
4.5
|
0.5*
|
0.04
|
0.01*
|
0.1*
|
-
|
Y-0.01
|
230®
|
57
|
5*
|
3*
|
22
|
2
|
14
|
0.5
|
0.4
|
0.5*
|
0.3
|
0.1*
|
0.1
|
0.015* |
- |
0.5*
|
La-0.02
|
233™ |
48 |
19 |
1.5* |
19 |
7.5 |
0.3* |
0.4* |
0.20* |
- |
3.3 |
0.5 |
0.1 |
0.004 |
0.03 |
- |
Ta-0.5,
Y-0.025* |
242®
|
65
|
1*
|
2*
|
8
|
25
|
-
|
0.8*
|
0.8*
|
-
|
0.5*
|
-
|
0.03*
|
0.006*
|
-
|
0.5*
|
-
|
244® |
61
|
1*
|
2*
|
8
|
22.5
|
6
|
0.8*
|
0.1*
|
-
|
0.5*
|
-
|
0.03*
|
0.006*
|
-
|
-
|
-
|
263
|
52
|
20
|
0.7*
|
20
|
6
|
-
|
0.4
|
0.2
|
-
|
0.6*
|
2.4*
|
0.06
|
0.005*
|
0.04*
|
0.2*
|
(Al+Ti)-2.6
|
282®
|
57
|
10
|
1.5*
|
20
|
8.5
|
-
|
0.3*
|
0.15*
|
-
|
1.5
|
2.1
|
0.06
|
0.005* |
- |
-
|
-
|
617
|
54
|
12.5
|
1
|
22
|
9
|
-
|
0.2*
|
0.2*
|
-
|
1.2
|
0.3
|
0.07
|
0.006*
|
-
|
-
|
-
|
625
|
62
|
1*
|
5*
|
21
|
9
|
-
|
0.5*
|
0.5*
|
3.7c
|
0.4*
|
0.4*
|
0.1*
|
-
|
-
|
0.5*
|
-
|
625SQ®
|
62
|
1*
|
5*
|
21
|
9
|
-
|
0.5*
|
0.15*
|
3.7c
|
0.4*
|
0.4*
|
0.03*
|
-
|
-
|
0.5*
|
N-0.02*
|
718
|
52
|
1*
|
19
|
18
|
3
|
-
|
0.35*
|
0.35*
|
5c
|
0.5
|
0.9
|
0.05
|
-
|
0.004
|
0.1*
|
-
|
B |
67 |
2.5* |
5 |
1* |
28 |
- |
1* |
1* |
- |
- |
- |
0.05* |
- |
- |
0.15* |
V-0.3 |
HR-160® |
37 |
29 |
2* |
28 |
1* |
1* |
0.5 |
2.75 |
1* |
0.4* |
0.5 |
0.05 |
- |
- |
0.5* |
- |
HR-224® |
47 |
2* |
27.5 |
20 |
0.5* |
0.5* |
0.5* |
0.3 |
0.15* |
3.8 |
0.3 |
0.05 |
0.004* |
0.025* |
- |
- |
HR-235® |
- |
- |
1.5* |
31 |
5.6 |
- |
0.65* |
0.6* |
1* |
0.4* |
0.5* |
0.06* |
- |
- |
3.8 |
- |
R-41 |
52 |
11 |
5* |
19 |
10 |
- |
0.1* |
0.5* |
- |
1.5 |
3.1 |
0.09 |
0.006 |
0.07* |
- |
- |
S |
67 |
2* |
3* |
16 |
15 |
1* |
0.5 |
0.4 |
- |
0.25 |
- |
0.02* |
0.015* |
- |
0.35* |
La-0.02 |
W |
63 |
2.5* |
6 |
5 |
24 |
1* |
1* |
1* |
- |
- |
- |
0.12* |
- |
- |
0.5* |
V-0.6* |
Waspaloy |
58 |
13.5 |
2* |
19 |
4.3 |
- |
0.1* |
0.15* |
- |
1.5 |
3 |
0.08 |
0.006* |
0.05 |
0.1* |
- |
X |
47 |
1.5 |
18 |
22 |
9 |
0.6 |
1* |
1* |
0.5* |
0.5* |
0.15* |
0.1 |
0.008* |
- |
0.5* |
- |
X-750
|
70b
|
1*
|
8
|
16
|
-
|
-
|
0.35*
|
0.35*
|
1c
|
0.8
|
2.5
|
0.08*
|
-
|
-
|
0.5*
|
-
|
aAs balance bMinimum cCb+Ta *Maximum
Cobalt-Base:
Alloy
|
Coa
|
Ni
|
Fe
|
Cr
|
Mo
|
W
|
Mn
|
Si
|
Cb
|
Al
|
Ti
|
C
|
B
|
Zr
|
Cu
|
Others
|
6B
|
58
|
2.5
|
3*
|
30
|
1.5*
|
4
|
1.4
|
0.7
|
-
|
-
|
-
|
1
|
-
|
-
|
-
|
-
|
25
|
51
|
10
|
3
|
20
|
1*
|
15
|
1.5
|
0.4*
|
-
|
-
|
-
|
0.10
|
-
|
-
|
-
|
-
|
188
|
39
|
22
|
3*
|
22
|
-
|
14
|
1.25*
|
0.35
|
-
|
-
|
-
|
0.10
|
0.015*
|
-
|
-
|
La-0.03
|
NS-163®
|
40
|
8
|
21
|
28
|
-
|
-
|
0.5*
|
0.5* |
1
|
0.5*
|
1.3
|
0.10
|
0.015*
|
-
|
0.2*
|
- |
aAs balance bMinimum cCb+Ta *Maximum
Iron-Base:
Alloy
|
Fea
|
Ni
|
Co
|
Cr
|
Mo
|
W
|
Mn
|
Si |
Cb
|
Ta
|
Al
|
C
|
N
|
B
|
Cu
|
Others
|
556®
|
31
|
20
|
18
|
22
|
3
|
2.5
|
1
|
0.4
|
0.3*
|
0.6
|
0.2
|
0.1
|
0.2
|
0.02*
|
-
|
Zr-0.02, La-0.02
|
HR-120®
|
33
|
37
|
3*
|
25
|
1*
|
0.5*
|
0.7
|
0.6
|
0.7
|
-
|
0.1
|
0.05
|
0.2
|
0.004
|
0.5*
|
Ti-0.2*
|
MULTIMET® |
30 |
20 |
20 |
21 |
3 |
2.5 |
1.5 |
1* |
1c |
- |
- |
0.12 |
0.15 |
- |
0.5* |
- |
aAs balance bMinimum cCb+Ta *Maximum